The analysis of the welding materials impact for the hot-dip galvanization process quality

DOI: https://doi.org/10.3846/mla.2019.10053

Abstract

The hot dip galvanizing process is the most popular long-term corrosion protection method for welded constructions. The article analyzes influence of shielding gas by reducing the zinc layer on the seams in MAG welding. The influence of shielding gases on the geometry of the seam and the slagging of the slag is analyzed. Advantages and disadvantages of the applied gas are presented and the thickness of the zinc layers is compared.


Article in Lithuanian.


Suvirinimo medžiagų įtakos karštojo cinkavimo proceso kokybei tyrimas


Santrauka


Karštojo cinkavimo procesas – populiariausias ilgaamžis suvirintų konstrukcijų apsaugos nuo atmosferos sukeliamos korozijos būdas. Deja, cinko sluoksnio storis ant virintinės siūlės ir pagrindinio metalo pasiskirsto nevienodai. Straipsnyje analizuojama, kaip virinant MAG būdu apsauginių dujų aplinkoje sumažinti ant siūlės susidarantį cinko sluoksnį. Analizuojama apsauginių dujų įtaka siūlės geometrijai ir šlako susiformavimui. Pateikiami naudojamų dujų pranašumai ir trūkumai, lyginamas cinko sluoksnio storis.


Reikšminiai žodžiai: MAG suvirinimo procesas, dujų mišiniai, pagrindinis metalas, cinko sluoksnis, karštasis cinkavimas.

Keyword : MAG welding process, gas mixtures, the main metal, zinc layer, hot-dip galvanizing

How to Cite
Rožėnė, J., Gedzevičius, I., & Mikaliūnas, Šarūnas. (2019). The analysis of the welding materials impact for the hot-dip galvanization process quality. Mokslas – Lietuvos Ateitis / Science – Future of Lithuania, 11. https://doi.org/10.3846/mla.2019.10053
Published in Issue
May 14, 2019
Abstract Views
611
PDF Downloads
512
Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

References

Boiko, I., & Avisans, D. (2013). Study of shielding gases for mag welding. Materials Physics and Mechanics, 16(3), 126-134. Retrieved from http://www.ipme.ru/e-journals/MPM/no_21613/MPM216_04_boiko.pdf

Bondareva, O. S., & Melnikov, A. A. (2016). Effect of the silicon content in steel on the hot-dip zinc coating microstructure formation. Materials and Technologies of New Generations in Modern Materials Science, 5(3), 5-21. Retrieved from http://iopscience.iop.org/article/10.1088/1757-899X/156/1/012015/pdf

S355 European Standard Steel. (2004). S355 EN 10025: 2004 Standard Structural Steel Plate Retrieved from http://www.joostdevree.nl/bouwkunde2/jpgs/staal_23_standaarden_s355_european_standard_steel.pdf

ISO/TR 16060. (2003). Destructive tests on welds in metallic materials – Etchants for macroscopic and microscopic examination. I dalis (tapatus ISO 16060:2003(E). Vilnius: Lietuvos standartizacijos departamentas (10 p.).